氧化锆/甲基丙烯酸甲酯复合材料的制备研究
引用本文:艾德生,马静玉,赵昆,戴遐明,高喆.氧化锆/甲基丙烯酸甲酯复合材料的制备研究[J].武汉理工大学学报,2007,29(10):89-92.
作者姓名:艾德生  马静玉  赵昆  戴遐明  高喆
作者单位:清华大学核能与新能源技术研究院,北京,100084
摘    要:纳米ZrO2颗粒经过偶联后,通过表面接枝法,制备表面接枝聚合物ZrO2-PMMA。沉降分析、红外光谱和光电子能谱的结果证明了聚合物确实是纳米ZrO2颗粒被PMMA所包覆,纳米ZrO2颗粒表面有机化后分散性能大大增加。

关 键 词:偶联  聚合
文章编号:1671-4431(2007)10-0089-04
修稿时间:2007-06-25

Research on Synthesis of ZrO2/MMA Composites
AI De-sheng,MA Jing-yu,ZHAO Kun,DAI Xia-ming,GAO Zhe.Research on Synthesis of ZrO2/MMA Composites[J].Journal of Wuhan University of Technology,2007,29(10):89-92.
Authors:AI De-sheng  MA Jing-yu  ZHAO Kun  DAI Xia-ming  GAO Zhe
Affiliation:Institute of Nuclear and New Energy, Tsinghua University, Beijing 100084, China
Abstract:ZrO2-PMMA surface-grafted polymer was prepared via 'grafted from' route,from ZrO2 nanoparticles which were firstly coupled.The results of sedimentation analysis,infrared spectrum and photoelectron spectrum proved that the polymer was composed of ZrO2 nanoparticles and PMMA.The dispersity of ZrO2 nanoparticles was enhanced greatly after the polymer formed.
Keywords:ZrO2-PMMA