Mechanical properties of rapidly solidified ribbons of some AI–Si based alloys

Continuous uniform ribbons of Al–16 Si, Al–12.5 Si–1 Ni and Al–12.5 Si–1 Mg were prepared by melt spinning. Microhardness was measured. The as-melt spun values were 1280, 1370 and 1500 MN m-2 which relax on thermal ageing to 700, 700 and 800 MN m-2 for Al–16 Si, Al–Si–Ni and Al–Si–Mg, respectively. The hardness values of the melt spun ribbons are higher than the as-cast rods from which the ribbons were produced by a factor ranging from 1.8–2.2 times. Tensile testing at room temperature shows that the load–elongation curves are linear with a change of slope occurring in some of the specimens. These curves also show serrations in the case of as-melt spun and the intermediately annealed Al–Si specimens, while no serration was observed in the fully annealed samples. No serration was observed in the Al–Si–Ni and Al–Si–Mg alloys. UTS values were 420, 270 and 100 MN m-2 for Al–16 Si, Al–Si–Ni and Al–Si–Mg, respectively. These values show that the rapid solidification process improved the tensile properties significantly in Al–16 Si and Al–Si–Ni alloys while no significant improvement can be detected for Al–Si–Mg alloy. A discussion is given on hardness relaxation and tensile testing results in terms of silicon precipitation. This revised version was published online in November 2006 with corrections to the Cover Date.