Hydrogen production by steam reforming of ethanol over Co/CeO2 catalysts: Effect of cobalt content |
| |
Authors: | Magdalena Greluk Marek Rotko Grzegorz Słowik Sylwia Turczyniak-Surdacka |
| |
Affiliation: | 1. Department of Chemical Technology, Faculty of Chemistry, Marie Curie-Sklodowska University, Maria Curie-Sklodowska Sq. 3, 20-031 Lublin, Poland;2. Biological and Chemical Research Centre, University of Warsaw, 101 ?wirki i Wigury Street, 20-089 Warsaw, Poland |
| |
Abstract: | The Co/CeO2 catalysts obtained by co-precipitation method were used in the steam reforming of ethanol (SRE). The influence of cobalt active phase content (15–29 wt%), the reaction temperature (420–600 °C) and H2O/EtOH molar ratio (12/1 and 6/1) were examined. The physicochemical characterization revealed that the cobalt content of the catalyst influences the metal-support interaction which results in catalyst performance in SRE process. The differences between catalytic properties of the Co/CeO2 catalysts with different metal loading in SRE process decayed at 500 °C for H2O/EtOH = 12/1. The best performance among the tested catalysts showed the 29Co/CeO2 catalyst with the highest cobalt content, exhibiting the highest ethanol conversion, selectivity to two most desirable products and the lowest selectivity to by-products in comparison with catalysts containing smaller amount of metal. Its catalytic properties results probably from its unique physicochemical properties, i.e this catalyst contains large amount of cobalt but the metal crystallites are relatively small. Regardless cobalt content, an increase in the water-to-ethanol molar ratio in the feed increased the concentration of hydrogen an carbon dioxide and decreased formation of carbon monoxide, acetone, aldehyde and ethylene. |
| |
Keywords: | Hydrogen production Ethanol steam reforming Cobalt Ceria |
本文献已被 ScienceDirect 等数据库收录! |
|