Effect of BaWO4 on the Microwave Dielectric Properties of Ba(Mg1/3Ta2/3)O3 Ceramics

Physical and microwave dielectric properties of complex perovskite Ba(Mg_1/3Ta_2/3)O₃ ceramics have been investigated as a function of the amount of BaWO₄ in the temperature range from 20° to 80°C at 10.5 GHz. Up to 0.05 mol BaWO₄ addition, the lattice constant ratio ( c/a ), ordering parameter, apparent density, and unloaded Q all increase, due to the increase in the substitution of Ta⁵⁺ ions of Ba(Mg_1/3Ta_2/3)O₃ by W⁶⁺ ions from the melted BaWO₄ at above 1430°C. With further addition of BaWO_4, the unloaded Q decreases, due to an increase of the BaWO₄ phase. The temperature coefficient of resonant frequency (TCF) can be controlled by the volume mixture rule of Ba(Mg_1/3Ta_2/3)O₃ and BaWO₄. When 0.09 mol BaWO₄ is added, TCF becomes 0 ppm/°C.