The role of lanthana loading on the catalytic properties of Pd/Al2O3-La2O3 in the NO reduction with H2

The role of La₂O₃ loading in Pd/Al₂O₃-La₂O₃ prepared by sol–gel on the catalytic properties in the NO reduction with H₂ was studied. The catalysts were characterized by N₂ physisorption, temperature-programmed reduction, differential thermal analysis, temperature-programmed oxidation and temperature-programmed desorption of NO.

The physicochemical properties of Pd catalysts as well as the catalytic activity and selectivity are modified by La₂O₃ inclusion. The selectivity depends on the NO/H₂ molar ratio (GHSV = 72,000 h⁻¹) and the extent of interaction between Pd and La₂O₃. At NO/H₂ = 0.5, the catalysts show high N₂ selectivity (60–75%) at temperatures lower than 250 °C. For NO/H₂ = 1, the N₂ selectivity is almost 100% mainly for high temperatures, and even in the presence of 10% H₂O vapor. The high N₂ selectivity indicates a high capability of the catalysts to dissociate NO upon adsorption. This property is attributed to the creation of new adsorption sites through the formation of a surface PdO_x phase interacting with La₂O₃. The formation of this phase is favored by the spreading of PdO promoted by La₂O₃. DTA shows that the phase transformation takes place at temperatures of 280–350 °C, while TPO indicates that this phase transformation is related to the oxidation process of PdO: in the case of Pd/Al₂O₃ the O₂ uptake is consistent with the oxidation of PdO to PdO₂, and when La₂O₃ is present the O₂ uptake exceeds that amount (1.5 times). La₂O₃ in Pd catalysts promotes also the oxidation of Pd and dissociative adsorption of NO mainly at low temperatures (<250 °C) favoring the formation of N₂.