Apatite-forming ability and magnetic properties of glass-ceramics containing zinc ferrite and calcium sodium phosphate phases |
| |
Authors: | Rajendra Kumar Singh A Srinivasan |
| |
Affiliation: | Department of Physics, Indian Institute of Technology Guwahati, Guwahati – 781039, India |
| |
Abstract: | Fine particles of zinc ferrite (ZnFe2O4) and calcium sodium phosphate NaCaPO4] were crystallized in bulk x(ZnO, Fe2O3)(65?x)SiO220(CaO, P2O5)15Na2O (6 ≤ x ≤ 21 mol %) glassy matrix by heat treatment. Initial magnetization curves reveal that samples with x = 6 and 9 mol % zinc–iron oxide exhibit both ferrimagnetic and paramagnetic contributions, whereas, samples with x > 9 mol % zinc–iron oxide exhibit only ferrimagnetic contribution. This observation is supported by the disappearance of the electron paramagnetic resonance (EPR) absorption line centered at g ≈ 4.3 in samples with x > 9 mol % zinc–iron oxide. Apatite-forming ability of the glass-ceramic samples was investigated by examining apatite formation on the surface of the samples treated in simulated body fluid (SBF). Increase in apatite-forming ability was observed with an increase in zinc–iron oxide content. The results obtained have been used to understand the evolution of the apatite surface layer as a function of immersion time in SBF and glass-ceramic composition. A good correlation has also been observed between the magnetic nature of the samples and their apatite-forming ability. These materials are expected to find application as thermo-seeds in hyperthermia treatment of bone cancer. |
| |
Keywords: | |
本文献已被 ScienceDirect 等数据库收录! |
|