Effect of H2/Ar plasma on growth behavior of ultra-nanocrystalline diamond films: The TEM study

Incorporation of H₂ species into Ar plasma was observed to markedly alter the microstructure of diamond films. TEM examinations indicate that, while the Ar/CH₄ plasma produced the ultrananocrystalline diamond films with equi-axed grains (~ 5 nm), the addition of 20% H₂ in Ar resulted in grains with dendrite geometry and the incorporation of 80% H₂ in Ar led to micro-crystalline diamond with faceted grains (~ 800 nm). Optical emission spectroscopy suggests that small percentage of H₂-species (< 20%) in the plasma leads to partially etching of hydrocarbons adhered onto the diamond clusters, such that the C₂-species attach to diamond surface anisotropically, forming diamond flakes, which evolve into dendrite geometry. In contrast, high percentage of H₂-species in the plasma (80%) can efficiently etch away the hydrocarbons adhered onto the diamond clusters, such that the C₂-species can attach to diamond surface isotropically, resulting in large diamond grains with faceted geometry. The field needed to turn on the electron field emission for diamond films increases from E₀ = 22.1 V/μm (J_e = 0.48 mA/cm² at 50 V/μm applied field) for 0% H₂ samples to E₀ = 78.2 V/μm (J_e < 0.01 mA/cm² at 210 V/μm applied field) for 80% H₂ samples, as the grains grow, decreasing the proportion of grain boundaries.