| 宽板坯包晶钢裂纹的原因分析与改进措施 |
| |
| 引用本文： | 王春芳. 宽板坯包晶钢裂纹的原因分析与改进措施[J]. 南钢科技与管理, 2006, 0(3): 1-4 |
| |
| 作者姓名： | 王春芳 |
| |
| 摘 要： | 根据中厚板卷厂连铸宽板坯投产以来的生产实践，包晶钢的纵裂纹发生率远高于其它钢种。通过分析包晶钢纵裂纹形成的原因，并采取相应的措施，使包晶钢的纵裂纹得到有效控制。
|
| 关 键 词： | 宽板坯 包晶钢 裂纹 |
Cause Analysis on Crack of Wide Slab for Peritectic Steel and its Countermeasures |
| |
| Wang Chunfang. Cause Analysis on Crack of Wide Slab for Peritectic Steel and its Countermeasures[J]. Nansteel Science Technology and Management, 2006, 0(3): 1-4 |
| |
| Authors: | Wang Chunfang |
| |
| Abstract: | The longitudinal crack rate of peritectic steel is much higher than other steel grades since wide slab was put into production at Wide Plate/Coil Plant. Some measures have been taken to control the longitudinal crack of peritectic steel by analyzing the causes. |
| |
| Keywords: | wide slab peritectic steel crack |