The interaction of hydrogen sulfide with lead- and barium–cadmium–zinc-stabilized poly(vinyl chloride)

Poly(vinyl chloride) polymers stabilized with tribasic lead sulfate discolor upon exposure to hydrogen sulfide gas as a result of lead sulfide formation. The discoloration occurs for samples in both cord and sheet forms and is shown to be a function of total H₂S exposure, reaching a limiting value that is determined by the amount of lead stabilizer used in the polymer formulation. The permeation and diffusion constants for H₂S through PVC stabilized with tribasic lead sulfate and with a liquid Ba–Cd–Zn formulation are found to be P_Pb = (6.0 ± 0.2) × 10^?9, P_BaCdZn = (5.2 ± 0.2) × 10^?9 (both in cm³ gas?cm film/cm² area?sec?cm Hg), D_Pb = (1.3 ± 0.2) × 10^?7 cm²/sec, and D_BaCdZn = (6.4 ± 0.6) × 10^?8 cm²/sec, all measured at 21°C. The stabilizing efficiencies of the formulations were assessed by HCl evolution measurements, which show that exposure to H₂S decreases the initial polymer stability for both Pb-stabilized and Ba–Ca–Zn-stabilized formulations. Protection of stabilized PVC formulations from diffusing hydrogen sulfide is thus advisable for long-term stability as well as for color integrity.