| 摘 要： | The flow softening is an important phenomenon during hot deformation of metallic materials.In the present work,a more evident flow softening of Ti-6 Al-4 V alloy when deformed in two-phase region was observed in coarser a grain sample,which was attributed to an accelerated dynamic transformation from harder α phase into β phases.Notably,full β microstructure was observed in coarse grain samples at strain of 1.2,while retained a phase was observed in fine a grain specimens.In the views of thermodynamics and crystallographic analysis,the in-depth mechanisms of dynamic transformation were further investigated.
|