Effects of different indentation methods on fatigue life extension of cracked specimens |
| |
| Authors: | S.M.J. Razavi M.R. Ayatollahi A. Amouzadi F. Berto |
| |
| Affiliation: | 1. Fatigue and Fracture Laboratory, Center of Excellence in Experimental Solid Mechanic and Dynamics, School of Mechanical Engineering, Iran University of Science and Technology, Tehran, Iran;2. Department of Mechanical and Industrial Engineering, Norwegian University of Science and Technology (NTNU), Trondheim, Norway |
| |
| Abstract: | In this paper, 3 different indentation methods have been investigated for crack arresting and fatigue life enhancement of cracked components. The influence of residual stresses induced by indentation on fatigue crack growth (FCG) rate was explored by experiments and numerical simulations. Fatigue tests were conducted on a group of specimens which were indented on the crack tip by various indentation load magnitudes. For another group of specimens, the double indentation and triple indentation methods were applied on the cracked specimens with the aim of obtaining proper residual stress fields that contribute to higher crack growth retardations. Both the numerical and experimental results revealed that the higher indentation loads led to larger domain of compressive residual stress around the crack tip and consequently to higher fatigue life extension. In addition, the triple indentation method resulted in more FCG retardation compared with single and double indentation methods. Furthermore, for the specimens repaired by double and triple indentation methods, indenting ahead of the crack tip led to retardation in more crack growth compared with the other horizontal positions of indentation. |
| |
| Keywords: | crack retardation elasto‐plastic indentation fatigue crack growth fatigue damage repair residual stress distribution |
|
|