Short‐crack thresholds and propagation in an AISI 4340 steel under the effect of SP residual stresses
Authors:L Patriarca  M Filippini  S Beretta
Affiliation:Department of Mechanical Engineering, Politecnico di Milano, 20156 Milan, Italy
Abstract:The effect of residual stresses induced by shot‐peening in a high‐strength AISI 4340 steel has been studied with the purpose of deriving a consistent fatigue model incorporating the results of fatigue crack growth experiments in the threshold region for a broad range of load ratio (R‐ratio ranging from ?2.5 to 0.7), and the effect of short cracks by means of a modified El‐Haddad model. The proposed model, taking into account the effect of crack closure and being capable to assess the conditions for fatigue propagation of short cracks partially embedded in the shot‐peened surface layer, was validated against constant amplitude fatigue experiments conducted in the endurance strength region, ie, for fatigue lives up to 107 cycles, with micronotched specimens in the presence of shot‐peening residual stresses. The proposed model was also validated by comparing the results of fatigue crack propagation simulations with fatigue crack growth experiments under variable amplitude loading, experimentally reproducing the combined effect of service fatigue loads and shot‐peening residual stresses.
Keywords:AISI 4340  compression‐precracking  defects  fatigue crack growth  shot‐peening
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司  京ICP备09084417号