The kinetics of ettringite formation and dilatation in a blended cement with β-hemihydrate and anhydrite as calcium sulfate |
| |
Authors: | Cecilie Evju Staffan Hansen |
| |
Affiliation: | aOptiroc AS, P.O. Box 216 Alnabru, N-0614 Oslo, Norway bMaterials Chemistry, Center for Chemistry and Chemical Engineering, Lund University, P.O. Box 124, S-221 00 Lund, Sweden |
| |
Abstract: | The phase formation, heat of hydration and dilatation in a blended cement consisting of 50 wt.% calcium aluminate cement, 25 wt.% Portland cement and 25 wt.% calcium sulfate were studied (w/c=1). The calcium sulfate was β-hemihydrate, anhydrite and mixes of the two. Kinetic expressions describing the ettringite formation in the pastes with the pure calcium sulfates were found. Hydration reactions were suggested and the phase development was compared to the hydration heat by mass and heat balances. When the calcium sulfate was 75 and 50 wt.% β-hemihydrate, the systems behaved as a linear combination of the 100 and 0 wt.% blends. At 25 wt.%, the hydration kinetics differed from the other blends. With only β-hemihydrate, the last 50% of ettringite formation was accompanied by expansion, mainly caused by interaction of crystals growing radially on cement grains. In the paste with only anhydrite, ettringite crystals grew in solution and produced no expansion. |
| |
Keywords: | Hydration Kinetics Thermodynamic calculations Expansion Ettringite |
本文献已被 ScienceDirect 等数据库收录! |
|