Kinetics and crystallization in pH‐sensitive free‐radical crosslinking polymerization of acrylic acid

Free‐radical crosslinking polymerization and crystallization of acrylic acid (AAc) were investigated by shear storage modulus (G′) measurements in pH 2, as well as in pH 6 and pH 10, by varying the molar ratio of crosslinking agent (N,N′‐methylene bis‐acrylamide; MBAAm) to AAc (0.583 × 10^?3, 1.169 × 10^?3, 1.753 × 10^?3, and 2.338 × 10^?3). Our results showed that the pre‐gelation time was the same at pH 2, regardless of the concentration of MBAAm. The propagation time was determined by the initial feed concentration of AAc, and the length of the linear curve in the propagation was proportional to the concentration of MBAAm. The Avrami exponent (n), as an indicative of growing pattern of an infinite molecule, in the crystallization was increased in proportional to the concentration of MBAAm, and generally low at pH 2. In the deceleration phase, n was observed near 1.0 throughout the all specimens. These results indicated that (1) the length of the pre‐gelation period was determined by the ionization of AAc (or pH), (2) the polymerization rate of AAc was not affected by the concentration of MBAAm, and (3) the inhomogeneity of hydrogel was determined by the growing pattern of infinite molecule in propagation phase. © 2015 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2015 , 132, 42195.