Development of Si_3N_4/Al composite by pressureless melt infiltration |
| |
作者单位: | Institute of |
| |
摘 要: | 1 Introduction Composites of ceramic/metal or metal/ceramic are expected to have properties superior to their constituents alone1?4]. However, the fundamental difference in atomic bonding between metals and ceramics results in quite different physical a…
|
Development of Si3N4/Al composite by pressureless melt infiltration |
| |
Authors: | Akhtar Farid GUO Shi-ju |
| |
Abstract: | Pressureless infiltration process to synthesize Si3N4/Al composite was investigated. Al-2%Mg alloy was infiltrated into Si3N4 and Si3N4 containing 10% Al2O3 preforms in the atmosphere of nitrogen. It is possible to infiltrate Al-2%Mg alloy in Si3N4 and Si3N4 containing 10% Al2O3 preforms. The growth of the dense composite of useful thickness was facilitated by the presence of magnesium powder at the interface and by flowing nitrogen. During infiltration Si3N4 reacted with aluminium to form Si and AlN, the growth of composite was found to proceed in two ways, depending on the Al2O3 content in the initial preform. Firstly, preform without Al2O3 content gives rise to AlN, Al3.27Si0.47 and Al type phases after infiltration. Secondly, perform with 10% Al2O3 content gives rise to AlN-Al2O3 solid solution phase (AlON), MgAl2O4, Al and Si type phases. AlON phase was only present in composite, containing 10% Al2O3 in the Si3N4 preforms before infiltration. |
| |
Keywords: | Si3N4 composite infiltration AlON AlN-Al2O3 solid solution |
本文献已被 CNKI 万方数据 等数据库收录! |
|