| 奥氏体不锈钢过热器常见失效形式分析 |
| |
| 引用本文： | 阎光宗,徐雪霞,张晓昱,柯浩,欧阳杰.奥氏体不锈钢过热器常见失效形式分析[J].河北电力技术,2011,30(3):52-54. |
| |
| 作者姓名： | 阎光宗 徐雪霞 张晓昱 柯浩 欧阳杰 |
| |
| 作者单位： | 河北省电力研究院,石家庄,050021 |
| |
| 摘 要： | 介绍奥氏体不锈钢过热器氧化皮脱落堵塞爆管、应力腐蚀开裂、原始缺陷开裂3种常见失效形式,分析失效原因,并提出相应的预防措施.
|
| 关 键 词： | 奥氏体不锈钢 过热器 失效 |
Analysis on Usual Failure of Austenitic Stainless Steel Superheater |
| |
| Affiliation: | Yan Guangzong,Xu Xuexia,Zhang Xiaoyu,et al |
| |
| Abstract: | The usual failure reason of the austenitic stainless steel such as blockage by oxidation scales fallen from the inner wall,stress corrosion,original disfigurement are analyzed.Relevant prevention measures aiming at the different failure cause are proposed. |
| |
| Keywords: | austenitic stainless steel superheater failure |