Catalytic-Oxidative Leaching of Low-Grade Complex Zinc Ore by Cu (II) Ions Produced from Copper Ore in Ammonia-Ammonium Sulfate Solution |
| |
| Authors: | Zhi Xiong Liu Zhou Lan Yin Hui Ping Hu Qi Yuan Chen |
| |
| Affiliation: | 1. College of Chemistry and Chemical Engineering, Jishou University, Jishou City, Hunan Province, 410083, P.R. China
2. School of Chemistry and Chemical Engineering, Central South University, Changsha City, Hunan, 410083, P.R. China
|
| |
| Abstract: | The catalytic-oxidative leaching of a mixed ore, which consists of low-grade oxide copper ore and oxide zinc ore containing ZnS, was investigated in ammonia-ammonium sulfate solution. The effect of the main parameters, such as mass ratio of copper ore to zinc ore, liquid-to-solid ratio, concentration of lixivant, leaching time, and temperature, was studied. The optimal leaching conditions with a maximum extraction of Cu 92.6?pct and Zn 85.5?pct were determined as follows: the mass ratio of copper ore to zinc ore 4/10?g/g, temperature 323.15?K (50?°C), leaching time 6?hours, stirring speed 500?r/min, liquid-to-solid ratio 3.6/1?cm3/g, concentration of lixivant including ammonia 2.0?mol/dm3, ammonium sulfate 1.0?mol/dm3, and ammonium persulfate 0.3?mol/dm3. It was found that ZnS in the oxide zinc ore could be extracted with Cu(II) ion, which was produced from copper ore and was used as the catalyst in the presence of ammonium persulfate. |
| |
| Keywords: | |
| 本文献已被 SpringerLink 等数据库收录！ |
|