Einfluß der Korngröße auf mechanische Eigenschaften und den ungeschmierten reversierenden Gleitverschleiß von Al2O3-Keramik

Influence of grain size on mechanical properties and dry oscillating sliding wear of Al₂O₃-ceramics Specimens with average grain sizes varying between about 0.8 μm and 12 μm were produced by cold isostatic pressing of high purity Al₂O₃-powder followed by sintering between 1300°C and 1700°C. Hardness, Young's modulus, bending strength and fracture toughness were measured as a function of average grain sizes. Tribological tests were carried out on the different microstructures at normal laboratory air and room temperature by using a ring-on-block tribometer. Experimental results showed the dependence of mechanical properties on grain size, hardness and bending strength obeying a Hall-Petch type relation, approximately. Coefficient of friction was relatively independent of grain size under the test conditions used. However, wear intensity increased substantially if a critical grain size was surpassed. This was due to a change in mechanisms of material removal which was confirmed by scanning electron microscopical studies of the worn surfaces.