Insight into the key aspects of the regeneration process in the NOx storage reduction (NSR) reaction probed using fast transient kinetics coupled with isotopically labelled NO over Pt and Rh-containing Ba/Al2O3 catalysts

For the first time, the coupling of fast transient kinetic switching and the use of an isotopically labelled reactant (¹⁵NO) has allowed detailed analysis of the evolution of all the products and reactants involved in the regeneration of a NO_x storage reduction (NSR) material. Using realistic regeneration times (ca. 1 s) for Pt, Rh and Pt/Rh-containing Ba/Al₂O₃ catalysts we have revealed an unexpected double peak in the evolution of nitrogen. The first peak occurred immediately on switching from lean to rich conditions, while the second peak started at the point at which the gases switched from rich to lean. The first evolution of nitrogen occurs as a result of the fast reaction between H₂ and/or CO and NO on reduced Rh and/or Pt sites. The second N₂ peak which occurs upon removal of the rich phase can be explained by reaction of stored ammonia with stored NO_x, gas phase NO_x or O₂. The ammonia can be formed either by hydrolysis of isocyanates or by direct reaction of NO and H₂.

The study highlights the importance of the relative rates of regeneration and storage in determining the overall performance of the catalysts. The performance of the monometallic 1.1%Rh/Ba/Al₂O₃ catalyst at 250 and 350 °C was found to be dependent on the rate of NO_x storage, since the rate of regeneration was sufficient to remove the NO_x stored in the lean phase. In contrast, for the monometallic 1.6%Pt/Ba/Al₂O₃ catalyst at 250 °C, the rate of regeneration was the determining factor with the result that the amount of NO_x stored on the catalyst deteriorated from cycle to cycle until the amount of NO_x stored in the lean phase matched the NO_x reduced in the rich phase. On the basis of the ratio of exposed metal surface atoms to total Ba content, the monometallic 1.6%Pt/Ba/Al₂O₃ catalyst outperformed the Rh-containing catalysts at 250 and 350 °C even when CO was used as a reductant.