Effects of current density on the corrosion behaviour of anodized aluminum alloy in FeCl3 solution |
| |
Authors: | CUI Xin-fang QIAO Ying-jie LIU Rui-liang LIAN Xiao-zheng |
| |
Affiliation: | School of Material Science and Chemical Engineering, Harbin Engineering University, Harbin 150001, China |
| |
Abstract: | In the present study,2024 aluminum alloy specimen was anodized in acetic acid and oxalic acid electrolytes.Effects of the current density on the microstructure and corrosion resistance of anodic oxide film have been investigated.The steady voltage increases from 11 V to 71 V with the current density increase from 0.5 A /dm2 to 2.5 A /dm2.The SEM reveals that there are pits,cavities and irregular pores in the anodic film,and their size and morphologies change with the current density.The corrosion resistance of the film was evaluated by potentiodynamic polarization and electrochemical impedance in 0.1 mol /L FeCl3 solution at room temperature.The results show that corrosion resistance of the anodic oxide film changes with the current density,and the anodic film formed at the current density of 1.0 A /dm2 has the best corrosion resistance.These observations indicate that anodic film formed at J = 1.0 A /dm2 can serve as a support material for the Cu micrometallic patterns. |
| |
Keywords: | aluminum alloy anodic oxide film corrosion resistance FeCl3 solution |
本文献已被 CNKI 维普 万方数据 等数据库收录! |
| 点击此处可从《哈尔滨工业大学学报(英文版)》浏览原始摘要信息 |
|
点击此处可从《哈尔滨工业大学学报(英文版)》下载全文 |