New epoxy resins. II. The preparation,characterization, and curing of epoxy resins and their copolymers

A polymer having high aromaticity and/or cyclic ring structures in the chain backbone usually gives high heat resistance and flame resistance. Five glycidyl ether-type epoxy resins are prepared from bisphenol A (DGEBA), 9,9-bis(4-hydroxyphenyl)fluorene (DGEBF), 3,6-dihydroxyspiro-fluorene-9,9′-xanthane] (DGEFX), 10,10-bis(4-hydroxyphenyl) anthrone (DGEA), and 9,9,10,10-tetrakis(4-hydroxyphenyl)anthracene (TGETA) in order to study structure–thermal stability–flame resistance property relationships. In this study, trimethoxyboroxine (TMB) and diaminodiphenylsulfone (DDS) are employed as the curing agents. The char yield at 700°C under a nitrogen atmosphere and the glass transition temperature (T_g) for the uncured resins decrease according to the sequence TGETA > DGEFX > DGEA > DGEBF > DGEBA. The Tg values for these cured epoxy resins are DGEBA < DGEBF < DGEFX < DGEA. A T_g for the TGETA is not obtainable but would be expected to be the highest. The char yields at 700°C of these cured epoxy resins have the same trend as the uncured resins. DGEBF, DGEFX, DGEA, and TGETA added to the DGEBA system show increases in the char yield, T_g, and oxygen index with increasing concentration of these novel epoxy resins.