| 掺Pt的SnO2薄膜气敏特性研究 |
| |
| 引用本文： | 白振华,潘国峰,孙以材,张效玮.掺Pt的SnO2薄膜气敏特性研究[J].传感器世界,2008,14(3):14-18. |
| |
| 作者姓名： | 白振华 潘国峰 孙以材 张效玮 |
| |
| 作者单位： | 河北工业大学微电子研究所,300130;河北工业大学信息工程学院 |
| |
| 摘 要： | 用直流磁控溅射法分别在si（111）基片及陶瓷基片上制备掺有Pt的Sn02薄膜，并进行500℃～700℃退火处理，对掺杂前后的薄膜进行XRD分析，测试各掺杂样品气敏特性。500℃退火后，掺杂样品对各种有机气体有较高的灵敏度，随着溅射时间的延长，气敏特性提高。700℃退火后，45min溅射的样品对氨气有很高的灵敏度和很好的选择性，最佳工作温度为220℃左右。随着掺杂时间延长，气敏特性降低。
|
| 关 键 词： | SnO2薄膜 磁控溅射 气敏特性 灵敏度 |
| 文章编号： | 1006-883(2008)03-0014-05 |
Investigation on Gas Sensing Properties of SnO2 Thin Films Doped With Pt |
| |
| Abstract: | Thin films SnO2 doped with Pt were prepared by DC magnetron sputtering on Si （lll） wafers and ceramic tubes. Afterwards, annealing was carded out respectively at 500℃ and 700℃. The structure was studied by XRD and the sensing properties were tested , the samples showed higher sensitivitytowards the organic vapor after 500℃ annealing. After 700℃ annealing, the samples with 45 minutes Pt-doping showed excellent selectivity and high sensitivity only towards ammonia vapor . The best operating temperature is 220℃. The sensing properties decreased with the doping time beyond 45 minutes. |
| |
| Keywords: | Sn02 thin films doped sputter sensing properties sensitivity |