Mechanical Properties and Crystal Structure of HDPE Induced by Small Amount of High-molecular-weight and Low-molecular-weight Polyethylene under Shear Stress Produced by Dynamic Packing Injection Molding

In order to better understand the effect of small amount of both high-molecular-weight polyethylene (HMWPE) and low-molecular-weight polyethylene (LMWPE) on the mechanical properties and crystal morphology under the shear stress field, the dynamic packing injection molding (DPIM) was used to prepare the oriented pure polyethylene samples and its blends ones with different contents of HMWPE and LMWPE. The experiment substantiated that the further improvement of tensile strength and impact stength along the flow direction (MD) of HDPE/HMWPE/LMWPE samples was achieved, while the tensile strength along the transverse direction (TD) still substantially exceeded that of conventional molding. When the contents of HMWPE and LMWPE were respectively 8% in blends, the tensile strength in both flow and transverse directions of the samples were highly enhanced, with improvements from 27.75 MPa to 115.43 MPa (about 316%), in MD and from 23MPa to 32.74 MPa (about 42.34%), in TD; besides the impact strength was improved from 21.55 KJ/m² to 72.6 KJ/m² (about 236.89%), in MD but decreased from 17 KJ/m² to 6.92 KJ/m² in TD. The obtained samples were characterized via DSC, WAXD and SEM. For HDPE/HMWPE/LMWPE, the shish-kebab structure which is composed of stretched chains (shish) and lamellae (kebab) was seen in the oriented region of DPIM samples and the spherulites existed in the oriented region of SPIM samples. Furthermore, the appropriate amount HMWPE and LMWPE (about 8%, respectively) blended into mixture can improve the thickness and the length of lamellae, and the degree of crystallinity in shear region by DPIM which were approved by DSC and SEM, at the same time, it can also enhance the intensity of orientation of lamellae in shear region confirmed by SEM and WAXD. The reason of improvement of mechanical properties is the existence of these thicker, longer and more orientated lamellae in shear region.