Mullite rod-enhanced porous SiC ceramics prepared at low temperature from photovoltaic waste

In this paper, porous SiC ceramics (PSCs) were fabricated from photovoltaic waste at low temperatures. The effects of different additives and sintering temperatures on PSCs were studied in detail. The temperature of PSCs preparation can be reduced to 850?°C by adding MoO₃ as catalyst. The PSCs are reinforced by mullite rods grown in-situ, they also have a high permeability coefficient due to their network structure. From 850?°C to 1200?°C, the open porosity of PSCs changed slightly, and was within 45.32?±?0.6%. The PSCs produced at 1000?°C had the highest gas permeability coefficient of 8.24?×?10^–11?m² and the highest flexural strength of 50.17?MPa. However, the same PSCs could not be fabricated at 850?°C when Y₂O₃ or CeO₂ were used as sintering aids. This study provides an environment-friendly method for reusing photovoltaic waste and reducing the cost of preparing PSCs.