| 热处理工艺对热轧带钢氧化皮结构及其耐蚀性的影响 |
| |
| 引用本文： | 周贤良,朱敏,余慧燕,华小珍,叶志国.热处理工艺对热轧带钢氧化皮结构及其耐蚀性的影响[J].材料热处理学报,2011,32(7). |
| |
| 作者姓名： | 周贤良 朱敏 余慧燕 华小珍 叶志国 |
| |
| 作者单位： | 1. 南昌航空大学材料科学与工程学院,江西南昌330063 教育部无损检测重点实验室,江西南昌330063
2. 南昌航空大学材料科学与工程学院,江西南昌,330063 |
| |
| 基金项目： | 国家自然科学基金(50871051); 教育部无损检测重点实验室基金(ZD200729003); 江西省教育厅重点实验室基金(DB200901399); 江西省自然科学基金(2009GZC5009) |
| |
| 摘 要： | 利用不同热处理工艺在热轧带钢表面形成不同组成与结构的氧化皮。采用SEM、XRD、LRS、干湿周期浸润腐蚀实验、EIS测试、开路电位测试对不同氧化皮热轧带钢在NaHSO3溶液中腐蚀行为进行了研究。研究表明,慢冷和炉冷所制热轧带钢氧化皮均由Fe2O3、Fe3O4、FeO和Fe组成,其中Fe2O3是微量的,前者含有更多的Fe3O4,后者含有更多的FeO。慢冷所制氧化皮致密、连续、厚度均匀;炉冷制备的氧化皮致密性较差,含有大量的缺陷。慢冷制备的氧化皮热轧带钢的耐蚀性要好于炉冷制备的热轧带钢的耐蚀性。
|
| 关 键 词： | 热轧带钢 氧化皮 腐蚀行为 耐蚀性 |
Structure and corrosion resistance of oxide scale formed on hot rolled strip by different heat treatment processes |
| |
| ZHOU Xian-liang,ZHU Min,YU Hui-yan,HUA Xiao-zhen,YE Zhi-guo.Structure and corrosion resistance of oxide scale formed on hot rolled strip by different heat treatment processes[J].Transactions of Materials and Heat Treatment,2011,32(7). |
| |
| Authors: | ZHOU Xian-liang ZHU Min YU Hui-yan HUA Xiao-zhen YE Zhi-guo |
| |
| Affiliation: | ZHOU Xian-liang1,2,ZHU Min1,YU Hui-yan1,HUA Xiao-zhen1,YE Zhi-guo1(1.School of Material Science and Engineering,Nanchang Hangkong University,Nanchang 330063,China,2.Key Laboratory of Nondestructive Test,Ministry of Education,China) |
| |
| Abstract: | Different component and structure of scales were formed on the surface of hot rolled strip by different heat treatment processes.Corrosion behavior of the hot rolled strip with different oxide scales in sodium bisulfite solution were investigated by means of SEM,XRD,LRS,cyclic wet-dry immersion corrosion test,electrochemical impedance spectroscopy(EIS) and corrosion potential test.The results show that oxide scales prepared by different heat treatment processes mainly consist of Fe3O4/FeO/Fe,as well as a sp... |
| |
| Keywords: | hot rolled strip oxide scale corrosion behavior corrosion resistance |