Wear and friction behavior of sand cast brake rotor made of A359-20 vol% SiC particle composites sliding against automobile friction material

The effect of load range of 30-100 N and speed range of 3-12 m/s on the wear and friction behavior of sand cast brake rotor made of A359-20 vol% SiC particle composites sliding against automobile friction material was investigated. Dry sliding frictional and wear behavior were investigated in a pin-on-disc type apparatus. Automobile friction material was used as pin, while the A359-20 vol% SiC particle composites formed the rotating disc. For comparison, the wear and friction behavior of commercially used cast iron brake rotor were studied. The results showed that the wear rate of the composite disc decreased with increasing the applied load from 30 to 50 N and increased with increasing the load from 50 to100 N. However, the wear rate of the composite disc decreased with increasing the sliding speed at all levels of load applied in the present work. For all sliding speeds, the friction coefficient of the composite disc decreased with applied load. The worn surfaces as well as wear debris were studied using scanning electron microscopy (SEM), energy dispersive X-ray (EDX) analyzer and X-ray diffraction (XRD) technique. At load of 50 N and speed range of 3-12 m/s, the worn surface of the composite disc showed a dark adherent layer, which mostly consisted of constituents of the friction material. This layer acted as a protective coating and lubricant, resulting in an improvement in the wear resistance of the composite.