Energetics of La2O3–HfO2–SiO2 Glasses

A series of La₂O₃–HfO₂–SiO₂ glasses, approximately along the join 0.73SiO₂–0.27( x HfO₂–(1? x )La₂O₃), 0< x <0.3), was prepared using containerless processing techniques (aerodynamic levitation combined with laser heating in oxygen). The enthalpy of formation and enthalpy of vitrification at 25°C were obtained from drop solution calorimetry of these glasses and appropriate crystalline compounds in a molten lead borate (2PbO–B₂O₃) solvent at 702°C. The enthalpy of formation from crystalline oxides was exothermic and became less exothermic with increasing HfO₂ content. Heat contents were measured by transposed temperature drop calorimetry and depended linearly on the HfO₂ content. Differential scanning calorimetry showed that both the onset glass transition and the onset crystallization temperature of these glasses increased with increasing HfO₂ content. Upon slow cooling in air, the glasses crystallized to a mixture of baddeleyite, cristobalite, lanthanum disilicate, and hafnon.