In situ synthesis and properties of Zr2Al3C4/ZrB2 composites

The Zr₂Al₃C₄/ZrB₂ composites are in situ synthesized by spark plasma sintering using Zr, Al, graphite, and B₄C powders as the initial materials. The introduction of ZrB₂ can not only evidently hinder the coarsening of Zr₂Al₃C₄ grains, but also benefit the densification and improve the hardness and Young’s modulus of the Zr₂Al₃C₄/ZrB₂ composites. When the ZrB₂ content is 20 vol.%, the composite shows an optimum fracture toughness value of 4.37 MPa m^1/2, about 20% higher than that of the monolithic Zr₂Al₃C₄. The unique mechanical properties can be mainly ascribed to the contribution of ZrB₂ as the reinforcing phase hindering the crack propagating. Compared with Zr₂Al₃C₄, the Zr₂Al₃C₄/20 vol.%ZrB₂ composite also exhibits a relatively higher thermal conductivity and better oxidation resistance.