Phase transformations of Ni-15 wt.% B powders during mechanical alloying and annealing

The formation of Ni-B binary intermetallic compounds was investigated by mechanical alloying (MA) of the Ni-15 wt.% B (≈ Ni-48 at.% B) powder mixture and subsequent heat treatment. It was found that an interstitial Ni(B) solid solution was formed at the early stage of milling, followed by the formation of Ni₃B intermetallic compound after 25 h of milling. On further milling, the Ni₃B transformed to Ni₂B and o-Ni₄B₃ (orthorhombic). Phase transformation during heating of Ni(B) solid solution phase up to 800 °C could be represented by Ni(B) → Ni₃B → Ni₂B. Other intermetallics can be formed by heat treatment of Ni(B) solid solution at temperatures above 800 °C.