Effect of in-situ formed MgO on the microstructure of thixomolded AZ91 magnesium alloy

ABSTRACT

In-situ magnesium matrix nano-composites were produced through a reaction of CO₂ with the AZ91 alloy at a semi-solid temperature range. The process was performed at 595°C, which corresponded to about 10% of solid fraction, under shear and mixing conditions generated by a screw-barrel system. As a result, nano-scale native MgO (30–50?nm) and a small amount of Al₄C₃ carbide within an eutectic consisting of α(Mg), β-Mg₁₇Al₁₂ were formed. Homogeneously distributed α(Mg) globular grains with volume 8–12% were visible. AZ91 composites revealed yield strength of 220?MPa at compression strength of 460?MPa and hardness 103?±?2?HV.