Microstructural and magnetic studies on P/M processed (Nd14.9Dy1.9)(Fe65.0Co8.0Cu1.0Ga1.0Nb0.7) B7.5 alloy

Sintered samples of (Nd_14.9 Dy_1.9) (Fe₆₅ Co₈ Cu_1.0 Ga_1.0 Nb_0.7)B_7.5 were prepared and subjected to stepwise annealing in the temperature range 875 K–675 K. The XRD and metallographic (optical and electron microscopy) studies reveal a multi-phase microstructure with each phase showing different solubility of the alloying additions. This alloy has T_C of 705 K with an intrinsic coercivity of 1000 kA/m and energy product of 250 kJ/m³ at RT. Solubility of Co into the matrix phase and that of Ga and Cu into the Nd-rich grain boundary phase are considered to be the main contributing factors for the significant enhancement in T_C and H_ci respectively of the multi-component alloy when compared to those of ternary NdFeB, wherein H_ci = 720 kA/m and T_C = 585 K.