Multiphase composites of tetragonal zirconia agglomerate dispersed into alumina and alumina-zirconia matrices

Multiphase composites of yttria- and ceria-doped tetragonal zirconia agglomerates (10–50 m) dispersed into an alumina or alumina-zirconia matrix were sintered at 1500–1600 °C in air, followed by post-Hot Isostatic Pressing (HIP) at 1450°C and 150 MPa in an Ar gas atmosphere. The relative density of the recovered composites was above 98% of the theoretical density. By chemically etching on the surface of zirconia agglomerates, the sinterability of composites was apparently improved; and no microcracks nor pores were observed at the interface of agglomerate and matrix. According to scanning electron microscopy (SEM) observation, tetragonal and tetragonal-monoclinic zirconia agglomerates were highly dispersed into the alumina or alumina-zirconia matrix. The multiphase composites containing 10 vol% spherical agglomerates demonstrate the relatively low value of bending strength, < 400 MPa, and a high value of fracture toughness, > 11 MPa m^1/2. The crack propagation introduced by Vickers indentation was efficiently suppressed and deflected by the agglomerates.