Determination of global and local residual stresses in SOFC by X-ray diffraction

Solid Oxide Fuel Cell (SOFC) is a high-performance electrochemical device for energy conversion. A single cell is composed of five layers made of different ceramic materials: anode support, anode functional layer, electrolyte, cathode functional layer and cathode. The mechanical integrity of the cell is a major issue during its lifetime, especially for the electrolyte layer. Damage of the cells is mainly due to the high operating temperature, the “redox” behaviour of the anode and the brittleness of the involved materials. Since residual stresses are known to play a significant role in the damage evolution, it is important to determine them.For this purpose, residual stresses in an anode-supported planar SOFC were measured by X-ray diffraction. Firstly, macroscopic stresses in each phase of each layer were studied using the sin²ψ method on a laboratory X-ray goniometer at room temperature. This technique enables the calculation of residual stress of the material from the measurement of the crystal lattice deformation. The electrolyte has been found under bi-axial compressive stress of ?920 MPa. Secondly, X-ray measurements controlling depth penetration were made in the electrolyte using grazing incidence method. The results show that the stress is not homogenous in the layer. The first five micrometers of the electrolyte have been found less constrained (?750 MPa) than the complete layer, suggesting a gradient of deformation in the electrolyte from the interface with the Anode Functional Layer to the free surface. Finally, local stress measurements were made on the electrolyte layer by X-ray synchrotron radiation that allows high accuracy measurement on the (sub-) micrometer scale. Polychromatic and monochromatic beams are used to determine the complete strain tensor from grain to grain in the electrolyte. First results confirm the macroscopic stress trend of the electrolyte. These X-ray techniques at different scales will contribute to a better understanding of the residual stress in the electrolyte layer and thus to the involved damage mechanisms.