Toughening of syndiotactic polypropylene with chalk

We hypothesized that polymer crystal anisotropy is advantageous for toughening of polymer composites involving easy slip network of oriented crystalline layers around filler particles. To this end, composites of syndiotactic polypropylene (sPP) with high concentration of submicrometer calcium carbonate particles were prepared and examined because usual sPP crystals exhibit high packing anisotropy. The specific orientation of sPP lamellae around chalk grains was found, which is supposed to facilitate the plastic deformation of polymer matrices. The compression molded bars of the composite exhibited markedly higher Izod impact strength than those of neat sPP. Toughening was even enhanced in the injection molded composite, for which 4.5‐fold increase in the impact strength was achieved. Injection‐induced orientation of the disordered form I sPP crystals was enhanced in the composite. The injection molded tensile specimens exhibited also a good drawability. Debonding at chalk–sPP interface occurred both during the impact and tensile tests facilitating the plastic deformation of sPP matrix. Chalk did not have any significant influence on the thermal properties of the composites but it affected the rheological behavior, increasing the loss and storage moduli, and the viscosity. Highly filled sPP composite exhibited solid‐like behavior in a molten state with the storage modulus exceeding the loss modulus in the entire frequency range. © 2016 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2016 , 133, 43651.