Abstract: | Continuous annealing treatment (austenitization for 4 hours followed by furnace cooling) and cyclic annealing treatment (four cycles of austenitization, each of 0.66 hours duration followed by forced air cooling) of 8.0 wt pct Cr white iron samples are undertaken at 1173 K, 1223 K, 1273 K, 1323 K, and 1373 K (900 °C, 950 °C, 1000 °C, 1050 °C, and 1100 °C) as steps of destabilizing the as-cast structure. Continuous annealing results in precipitation of secondary carbides on a matrix containing mainly pearlite, while cyclic annealing treatment causes similar precipitation of secondary carbides on a matrix containing martensite plus retained austenite. On continuous annealing, the hardness falls below the as-cast value (HV 556), while after cyclic annealing treatment there is about 70 pct increase in hardness, i.e., up to HV 960. Decrease in hardness with increasing annealing temperature is quite common after both heat treatments. The as-cast notched impact toughness (4.0 J) is nearly doubled by increasing to 7.0 J after both continuous and cyclic annealing treatment at 1173 K and 1223 K (900 °C and 950 °C). Cyclic annealing treatment gives rise to a maximum notched impact toughness of 10.0 J at 1373 K (1100 °C). Abrasive wear resistance after continuous annealing treatment degrades exhibiting wear loss greater than that of the as-cast alloy. In contrast, samples with cyclic annealing treatment show reasonably good wear resistance, thereby superseding the wear performance of Ni-Hard IV. |