Static recrystallization behavior of Inconel 718 alloy during thermal deformation |
|
| Authors: | Xianping Wei Wenjie Zheng Zhigang Song Ting Lei Qilong Yong Qingcheng Xie |
| Affiliation: | 1. Faculty of Metallurgical and Energy Engineering, Kunming University of Science and Technology, Kunming, 650093, China 2. Central Iron and Steel Research Institute, Beijing, 100081, China 3. No.704 Institute of China Shipbuilding Industry Corporation, Shanghai, 200031, China |
| Abstract: | The softening behavior of Inconel 718 alloy at different temperatures was studied using two-stage interrupted compression method on Gleeble1500D thermal stimulator, and the 2% offset method was applied to analyze the experimental dates. Finally, the static recrystallization fraction was obtained. At the same times, optical microscope (OM) and transmission electron microscopy (TEM) were employed to investigate the microstructure characteristic. The experimental results showed that the recrystallization was more sensitive to temperature than holding time. The recrystallization process finished quickly above 1 050 °C, and significantly prolonged below 1 025 °C. Additionally, the dynamical model of static recrystallization follows the Avrami equation. The nucleating mechanism was characterized by bulging at grain boundary and merging of sub-grain. |
| Keywords: | Inconel 718 ahoy static recrystallization nucleating mechanism |
| 本文献已被 CNKI 维普 SpringerLink 等数据库收录！ | |