| 稀土对碳素钢在模拟工业性大气腐蚀环境下耐蚀性的影响 | |
| 引用本文： | 汪兵,刘清友,王向东,文小明,毛新平.稀土对碳素钢在模拟工业性大气腐蚀环境下耐蚀性的影响[J].钢铁研究学报,2009,21(8):35-0. |
| 作者姓名： | 汪兵 刘清友 王向东 文小明 毛新平 |
| 作者单位： | 1. 钢铁研究总院先进钢铁流程及材料国家重点实验室,北京,100081 2. 本溪钢铁(集团)有限责任公司技术中心,辽宁本溪,117000 3. 广州钢铁企业集团有限公司技术中心,广东广州,510381 |
| 基金项目： | 国家自然科学基金，国家重点基础研究发展规划(973计划) |
| 摘 要： | 利用浸泡、电化学方法研究了Ce/La混和稀土对碳素钢在腐蚀介质中的缓蚀作用，采用相分析、周浸、锈层分析等方法研究了稀土对碳素钢耐工业性大气腐蚀性能的影响。结果表明：在模拟工业性大气腐蚀环境的酸性NaHSO3溶液中，稀土丝分解后生成的稀土离子是一种混合型缓蚀剂；在对碳素钢的缓蚀过程中，Ce/La离子沉积于同一区域；随钢中稀土含量增加，钢中相界固溶稀土和稀土/铁金属间化合物总量增加，钢的耐蚀性得到大幅度提高。另外，还对稀土减缓钢铁腐蚀过程进行了讨论，提出了稀土对碳素钢的缓蚀机理。 |
| 关 键 词： | 稀土 大气腐蚀 耐候钢 缓蚀剂 |
| 收稿时间： | 1900-01-01; |
Effect of Rare Earth on Corrosion Resistance of Carbon Steel in Simulated Industrial Atmospheric Environment |
|
| WANG Bing,LIU Qing-you,WANG Xiang-don,WEN Xiao-ming,MAO Xin-pin.Effect of Rare Earth on Corrosion Resistance of Carbon Steel in Simulated Industrial Atmospheric Environment[J].Journal of Iron and Steel Research,2009,21(8):35-0. | |
| Authors: | WANG Bing LIU Qing-you WANG Xiang-don WEN Xiao-ming MAO Xin-pin |
| Affiliation: | 1. State Key Laboratory of Advanced Steel Processing and Products, Central Iron and Steel Research Institute, Beijing 100081, China;2. Technology Centre, Benxi Iron and Steel Group Limited Company, Benxi 117000, Liaoning, China; 3. Technology Centre, Guangzhou Iron and Steel Enterprises Group Company, Guangzhou 510381, Guangdong, China |
| Abstract: | The inhibiting corrosion character of RE in the corrosion solution has been investigated by immersion and electrochemical test, and the effect of RE (rare earth) on the improvement of the simulated industrial atmospheric corrosion resistance of steel has been investigated by phase analysis, cyclic immersion corrosion test and rust layer analysis. The results showed that RE (rare earth) ion was one kind of mixed inhibitor generated by RE filament decomposed in NaHSO3 solution; due to the increase of RE content in the steel, the total amount of phase boundary solid solution RE and RE/Fe intermetallic compound increased, and the corrosion resistance of steel was improved largely. The theory of inhibiting corrosion of RE in the steel was brought forward. |
| Keywords: | rare earth atmospheric corrosion weathering steel corrosion inhibitor |