复极电解槽技改总结
引用本文:江新成,王远君.复极电解槽技改总结[J].氯碱工业,2010,46(6):13-15.
作者姓名:江新成  王远君
作者单位:昊华西南化工有限责任公司,四川,自贡,643000
摘    要:针对电解槽运行过程中相继出现的阳极法兰腐蚀严重、阳极网凹陷变形、阳极边网与边框焊点脱焊等设计缺陷问题,更换新网时对电极板阳极室进行技术改造,并增加电解单元,不仅解决了出现的问题,而且增加了装置能力。

关 键 词:电解槽  离子膜  单元槽  极网  电极  腐蚀

Summary on technical innovation of bipolar electrolyzers
JIANG Xincheng,WANG Yuanjun.Summary on technical innovation of bipolar electrolyzers[J].Chlor-Alkali Industry,2010,46(6):13-15.
Authors:JIANG Xincheng  WANG Yuanjun
Affiliation:( Southwest China Haohua Chemical Co. , Ltd. , Zigong 643000, China)
Abstract:The problems occurred sequentially during running of electrolyzers, including serious corrosion of anode flanges, depressed deformation of anode nets, weld crack between edges of anode nets and edges of frames. Design defects accounted for these problems. According to the above problems, the anode compartments in electrode plates were technical innovated when changing to new nets, and the number of electrolysis units were increased, and thus the problems were solved and the capacity of the facility were increased.
Keywords:electrolyzer  ion - exchange membrane  unit cell  electrode net  electrode  corrosion