Influence of Additives Ceria and Lanthana on Performance of Pd／Al／Monolith Honeycomb Catalysts

The effects of ceria and lanthana additives on activity and thermal stabilization of the catalysts for CO oxidation were studied. The results show that the addition of CeO2 clearly improves the catalytic activity, which may derive from the synergic effect between CeO2 and PdO. The catalysts were characterized by means of temperature-programmed reduction (TPR) and X-ray photoelectron spectroscopy (XPS) measurements. The XPS results of a slight increase in metal oxidation state reflect that the charge transfers from metal to ceria and ceria is slightly reduced, which leads to a decrease of the Ce-O bond strength. Pd-Ce synergism affects the reduction behavior of the catalysts. The TPR results show that the CeO2 ad-dition lowers the reduction temperature of PdO, while palladium facilitates the reduction of the ceria. For PdO/La2O3/Al2O3/monolith honeycomb catalysts, the aging test measurements at 1050 ℃ and the XRD results show that the formation of LaAlO3 which neutralizes the surface alumina defects inhibits the sintering of alumina.

Influence of Additives Ceria and Lanthana on Performance of Pd/Al/Monolith Honeycomb Catalysts

The effects of ceria and lanthana additives on activity and thermal stabilization of the catalysts for CO oxidation were studied. The results show that the addition of CeO2 clearly improves the catalytic activity, which may derive from the synergic effect between CeO2 and PdO. The catalysts were characterized by means of temperature-programmed reduction (TPR) and X-ray photoelectron spectroscopy (XPS) measurements. The XPS results of a slight increase in metal oxidation state reflect that the charge transfers from metal to ceria and ceria is slightly reduced, which leads to a decrease of the Ce-O bond strength. Pd-Ce synergism affects the reduction behavior of the catalysts. The TPR results show that the CeO2 addition lowers the reduction temperature of PdO, while palladium facilitates the reduction of the ceria. For PdO/La2O3/Al2O3/monolith honeycomb catalysts, the aging test measurements at 1050 ℃ and the XRD results show that the formation of LaAlO3 which neutralizes the surface alumina defects inhibits the sintering of alumina.