Microstructure and mechanical properties of Al2O3-Cr2O3 composite coatings produced by atmospheric plasma spraying

Al₂O₃, Al₂O₃-Cr₂O₃ and Cr₂O₃ coatings were deposited by atmospheric plasma spraying. Phase composition of powders and as-sprayed coatings was determined by X-ray diffraction. Electron probe microanalyzer was employed to investigate the polished and fractured surface morphologies of the coatings. Mechanical properties including microhardness, fracture toughness and bending strength were evaluated. The results indicate that the addition of Cr₂O₃ is conducive to the stabilization of α-Al₂O₃. Compared with the pure Al₂O₃ and Cr₂O₃ coatings, Al₂O₃-Cr₂O₃ composite coatings show lower porosities and denser structures. Heterogeneous nucleation of α-Al₂O₃ occurs over the isostructural Cr₂O₃ lamellae and partial solid solution of Al₂O₃ and Cr₂O₃ might be occurring as well. Furthermore, grain refining and solid solution strengthening facilitate the mechanical property enhancement of Al₂O₃-Cr₂O₃ composite coatings.