| c轴取向的M-型SLFCO铁氧体薄膜的制备及磁性能 | |
| 引用本文： | 訾振发,吕建国,刘红艳,方林,刘强春,朱雪斌,戴建明. c轴取向的M-型SLFCO铁氧体薄膜的制备及磁性能[J]. 功能材料, 2011, 42(8) |
| 作者姓名： | 訾振发 吕建国 刘红艳 方林 刘强春 朱雪斌 戴建明 |
| 作者单位： | 1. 合肥师范学院物理与电子工程系,安徽合肥230601／淮北师范大学物理与电子信息学院,安徽淮北235000／中科院固体物理研究所材料物理重点实验室,安徽合肥230031 2. 合肥师范学院物理与电子工程系,安徽合肥,230601 3. 淮北师范大学物理与电子信息学院,安徽淮北,235000 4. 中科院固体物理研究所材料物理重点实验室,安徽合肥,230031 5. 淮北师范大学物理与电子信息学院,安徽淮北235000／中科院固体物理研究所材料物理重点实验室,安徽合肥230031 |
| 基金项目： | 国家自然科学基金资助项目(51002156); 安徽省自然科学基金资助项目(11040606M56); 安徽省重点科研计划资助项目(09020204031); 合肥师范学院院级自然科学重点资助项目(2010kj03zd) |
| 摘 要： | 采用化学溶液沉积法在Al2O3（001）单晶衬底上制备SLFCO铁氧体薄膜,XRD谱表明样品具有c轴取向的单相结构,空间群为P63/mmc;AFM结果表明样品颗粒呈柱状,平均颗粒尺寸在50～100nm之间。SLFCO铁氧体薄膜具有高的室温饱和磁化强度（130A/m）,矫顽力（549.24kA/m）和大的矩形比（0.9）,这些性能表明SLFCO铁氧体薄膜是一种非常有潜在应用价值的高密度磁记录材料。 |
| 关 键 词： | SLFCO铁氧体薄膜 化学溶液沉积法 磁各向异性 |
Preparation and magnetic properties of c-axis oriented M-type SLFCO ferrite film via CSD method |
|
| ZI Zhen-fa,,,LV Jian-guo,LIU Hong-yan,FANG Lin,LIU Qiang-chun,ZHU Xue-bin,DAI Jian-ming. Preparation and magnetic properties of c-axis oriented M-type SLFCO ferrite film via CSD method[J]. Journal of Functional Materials, 2011, 42(8) | |
| Authors: | ZI Zhen-fa LV Jian-guo LIU Hong-yan FANG Lin LIU Qiang-chun ZHU Xue-bin DAI Jian-ming |
| Affiliation: | ZI Zhen-fa1,2,3,LV Jian-guo1,LIU Hong-yan2,FANG Lin2,LIU Qiang-chun2,ZHU Xue-bin3,DAI Jian-ming2,3(1.Department of Physics and Electronic Engineering,Hefei Normal University,Hefei 230601,China,2.School of Physics and Electronic Information,Huaibei Normal University,Huaibei 235000,3.Key Laboratory of Materials Physics,Institute of Solid State Physics,Chinese Academy of Sciences,Hefei 230031,China) |
| Abstract: | In this paper,Sr0.8La0.2Fe11.8Co0.2O19 ferrite film had been prepared on(00l) sapphire substrate via the chemical solution deposition method.Structural characteristics indicated that the film was c-axis oriented and single-phase with the space group P63/mmc.The grains were regular columnar and the sizes were in diameter between 50 and 100nm by AFM results.The sample had high saturation magnetization(130A/m),high coercivity(549.24kA/m),and large squareness ratio(0.9) at room temperature,which made it a promi... |
| Keywords: | SLFCO ferrite film chemical solution deposition method magnetic anisotropy |