P-type 4H and 6H-SiC high-voltage Schottky barrier diodes

High-voltage Schottky barrier diodes have been successfully fabricated for the first time on p-type 4H- and 6H-SiC using Ti as the barrier metal. Good rectification was confirmed at temperatures as high as 250°C. The barrier heights were estimated to be 1.8-2.0 eV for 6H-SiC and 1.1-1.5 eV for 4H-SiC at room temperature using both I-V and C-V measurements. The specific on resistance (R_on,sp) for 4H- and 6H-SiC were found to be 25 mΩ cm^-2 and 70 mΩ cm^-2 at room temperature. A monotonic decrease in resistance occurs with increasing temperature for both polytypes due to increased ionization of dopants. An analytical model is presented to explain the decrease of R_on,sp with temperature for both 4H and 6H-SiC which fits the experimental data. Critical electric field strength for breakdown was extracted for the first time in both p-type 4H and 6H-SiC using the breakdown voltage and was found to be 2.9×10⁶ V/cm and 3.3×10⁶ V/cm, respectively. The breakdown voltage remained fairly constant with temperature for 4H-SiC while it was found to decrease with temperature for 6H-SiC