Lattice rotation and stability of 22.5° ND rotated cube orientation in cold rolled polycrystalline AA 5182 aluminum alloy

AA 5182 aluminum alloy with a strong cube texture was cold rolled to different reductions at an angle of 22.5° to the prior rolling direction. The texture evolution at this new rolling direction was investigated by X-ray diffraction. The rotation paths and stability of the 22.5° ND rotated cube orientation were determined based on the variation in the three-dimensional orientation distribution function (ODF) with rolling reduction. The results show that most of the grains with the 22.5° ND rotated cube orientation are directly rotated to the β fiber along different rotation paths, but there are a few grains moving through the cube orientation to the β fiber. The {0 0 1}<1 1 0> oriented grains possess the lowest stability during rolling, and the stability increases as the initial orientation changes from the {0 0 1}<1 1 0> orientation to the {0 0 1}<1 0 0> orientation along the ₁ axis.