FeWO4Cl as cathode material for lithium rechargeable battery |
|
| Authors: | Sookhyeon Im Jinhee Park Heesung Oh Jinho Choy Claude Delmas Kyooseung Han |
| Affiliation: | 1. Department of Fine Chemical Engineering and Chemistry, Chungnam National University, 220 Kung, Youseong, Taejeon, 305-764, South Korea 2. Department of Chemistry, Ewha Womans University, Seoul, South Korea 3. Institut de Chimie de la Matière Condensée de Bordeaux, Av. Dr. A. Schweitzer, 33608, Pessac Cedex, France |
| Abstract: | Lithium has been electrochemically and chemically intercalated into layered FeWO4Cl. The discharge curve between FeWO4Cl and Li2FeWO4Cl is constituted by three potential plateaux and two domains where the cell voltage decreases rapidly upon the intercalation of lithium ions. A wide bi-phase domain is obtained for x in Li x FeWO4Cl ranging between 0.0 and 0.85. The limit of a solid solution extends in the vicinity of the LiFeWO4Cl composition. The theoretical and practical discharge capacities for Li1???xFeWO4Cl are 79.03 mAh/g and 78.45 mAh/g respectively. The structures of FeWO4Cl and LiFeWO4Cl were determined: from single crystal analysis and by Rietveld refinement of the powder X-ray diffraction pattern respectively. The modifications of the Fe–O bond lengths emphasize the iron reduction during the discharge process. Moreover, the strong change of Fe–Cl distance suggests a reversible framework modification. |
| Keywords: | |
| 本文献已被 SpringerLink 等数据库收录！ | |