Effects of substrate temperature on electrical and optical properties ITO films deposited by r.f. magnetron sputtering

Indium tin oxide (ITO) films have been prepared by r.f. magnetron sputtering using powder target. X-ray diffraction analysis indicates that the deposited films were polycrystalline and retained a cubic bixbite structure. The ITO films deposited at low substrate temperature (T _s) exhibit a (411) preferred orientation but the films deposited at high T _s prefer a (111) orientation. The substrate temperature was found to significantly affect the electrical properties. As the T _s was increased, the conductivity of ITO films was improved due to thermally induced crystallization. The lowest resistivity (8.7?×?10^?4 Ω-cm) was obtained from ITO films deposited at 450 °C. However, optical properties of the films were somewhat deteriorated. The infrared (IR) reflectance of the film increases with increasing the substrate temperature.