Widerstand der Schweißverbindungen kohlenstoffarmer und mit Molybdän legierter korrosionsbeständiger Stähle gegen interkristalline und Messerlinienkorrosion |
| |
Authors: | V íhal N Lehk K Matuka |
| |
Affiliation: | V. Číhal,N. Lehká,K. Matuška |
| |
Abstract: | Resistance to intercrystalline and knifeline corrosion of welds in low carbon stainless steels containing molybdenum Welds in steels containing (%) 0,019–0,080 C, 1,00–1,56 Mn, 0,03–0,92 Si, 0–0,026 P, 0–0,018 S, 10–13,60 Ni, 16–20,50 Cr, 0–3 Mo, 0–0,057 Ti, 0–0,87 Nb, prepared by electroslag and automatic submerged arc welding are as a general rule not susceptible to intercrystalline and knifeline corrosion; a certain susceptibility encountered with the Mo containing types can be largely eliminated by sensibilizing at 650 °C. Differences in the corrosion behaviour between base metal and weld seam could not be encountered; in some cases the weld metal turned out to be even more resistant. The test solutions used were: sulfuric acid + Cu sulfate + Cu, boiling, 48 hrs, and 65% nitric acid, boiling, 3 · 48 hrs. |
| |
Keywords: | |
|
|