TEM studies of cross sections of oxidized Fe-25Cr-6Al-La alloy

The oxidation behavior of the alloy Fe–25%Cr–6%Al-RE (rich in lanthanum) was investigated by means of TEM analysis. The results show that after 2 hr oxidation of the alloy, in pure oxygen at 1200° C, La precipitated in the oxide scale at the top of -Al₂O₃ grains and at the grain-boundary regions in the form of tiny particles of hexagonal La₂O₃. These tiny particles prevented aluminum from diffusing toward the surface and suppressed lateral growth of the oxide scale. The rare-earth constituents accelerated the internal oxidation of the alloy during thermal cycling between 1200° C and room temperature. They appeared as particles of aluminum oxide and lanthanum oxide. Particles of cubic La₂O₃ precipitated in the alloy matrix near the oxide scale-metal interface in a direction parallel to grain boundaries.