Effect of welding parameters on Al/Ti joint property in electron beam welding-brazing |
| |
Authors: | Wang Yarong Yu Yang and Teng Wenhua |
| |
Affiliation: | Institute of Machinery of Manufacturing Technology, China Academy of Engineering Physics, Mianyang, 621900 |
| |
Abstract: | The electron beam welding-brazing being used to join 5A06 Al alloy to TC4 Ti alloy decreases the formation of brittle intermetallic compound.Experiments were carried out to study the influence of electron beam welding parameters on the tensile strength of welds,based on an orthogonal test and analysis method.The welding parameters include beam current,welding speed,scanning figure,scanning frequency,figure size,beam offset and focus current.The optimum parameters for3 mm 5A06 Al alloy and 2 mm TC4 alloy were as follows:acceleration voltage was 60 kV,beam current was 11 mA,welding speed was 600 mm/min,focus current was 0 mA,scan figure was O,scanning frequency was 1 000 Hz and beam offset was 0.5 mm.The results show that the joints were with good appearance and quality welded by the optimum parameters.The successful joints could be gained and the maximum tensile strength of Al/Ti dissimilar alloy joints could be up to 222.61 MPa using electron beam welding-brazing. |
| |
Keywords: | Al alloy Ti alloy electron beam welding-brazing orthogonal test and analysis |
本文献已被 CNKI 万方数据 等数据库收录! |
| 点击此处可从《中国焊接》浏览原始摘要信息 |
|
点击此处可从《中国焊接》下载全文 |
|