Fabrication and Mechanical Properties of Continuously Graded MoSi2–ZrO2(2Y) Materials Using Wet-Molding |
| |
Authors: | Kenji Arata Nobutaka Takeuchi Masaru Yoshinaka Ken Hirota Osamu Yamaguchi |
| |
Affiliation: | Department of Molecular Science and Technology, Faculty of Engineering, Doshisha University, Tanabe Kyoto 610–03, Japan |
| |
Abstract: | Continuously graded MoSi2-ZrO2(2Y) materials with high density (97.5% of theoretical) have been fabricated by uniaxial wet-molding, followed by hot pressing (1000°C/1 h/30 MPa) and hot isostatic pressing (1400°C/2 h/196 MPa). Their composition profiles are greatly influenced by the viscosity of mixed solutions of glycerin and ethanol used as a dispersion medium; a linear compositional gradient from MoSi2/ZrO2(2Y) 70/30 to 20/80 mol% is obtained from the solution (50/50 vol%) with a viscosity of 20 mPa s. Vickers hardness (Hv) and fracture toughness (KIC) increase from 9.7 to 12.4 GPa and from 5.1 to 12.5 MPa m1/2, respectively, with increasing ZrO2(2Y) composition. |
| |