Physico-chemical characterization of hybrid polymers obtained by 2-hydroxyethyl(methacrylate) and alkoxides of zirconium |
| |
Authors: | R Di Maggio L FambriP Mustarelli R Campostrini |
| |
Affiliation: | a Department of Materials Engineering and Industrial Technologies, University of Trento, Via Mesiano, 77-38050 Trento, Italy b Department of Physical Chemistry, University of Pavia and I.N.F.M. Via Taramelli, 16 27100 Pavia, Italy |
| |
Abstract: | Hybrid monolithic materials were prepared through polymerisation of 2-hydroxyethyl methacrylate (HEMA) mixed with zirconium alkoxides (Zr(OBun)4, Zr(OPrn)4 and Zr(OEt)4), modified by acetylacetonate groups. The molar ratio HEMA/Zr varied between 1 and 4. Thermo-Gravimetry coupled with Mass Spectroscopy (TG-MS) analyses, 13C MAS NMR and Dynamical Mechanical Thermal Analysys (DMTA) indicated the polymeric chains were interconnected by the inorganic component.The presence of zirconium alkoxides modified substantially the poly-HEMA properties. Glass transition temperature of hybrid materials derived from butoxy and propoxy was found in the range 50-80 °C, depending on the composition. The typical swelling of p-HEMA in the water, was suppressed by the presence of zirconium compounds. After immersion in distilled water, hybrid polymers showed an initial slight weight increase, followed by a small mass loss, which increases proportionally to the length of alkoxyl group (ethoxide(propoxide(butoxide) and reaches a constant value after about 40 days. The hybrids remained always rigid and transparent. Flexural modulus and strength of about 400-900 and 4-8 MPa were measured. |
| |
Keywords: | Hybrid polymers 2-hydroxyethyl(methacrylate) HEMA |
本文献已被 ScienceDirect 等数据库收录! |
|